نموذج: C68700 15.88X2.11X1840MM
محيط: أنبوب نحاسي مستقيم
تطبيق: تكييف هواء أو ثلاجة, سخان الماء, أنبوب تبريد الزيت
سواء سبيكة: هل سبيكة
مكان المنشأ: الصين
| Material: | C68700 ,CuZn20Al2As,HAL77-2 | Standard: | ASTM B111, ASTM B88, ASTM B288 , ASTM B688 |
|---|---|---|---|
| Type Of Productis: | Seamless Tube, Welded Tube , Copper Fitting , Copper Fin Tube | TPI: | BV, SGS, IEI, MOODY, .... |
| NDT: | ET, UT,HT, PT | ||
| High Light: |
C68700 Aluminium Brass Tube,ASTM B111 Aluminium Brass Tube,ASME SB111 Aluminium Brass Tube |
||
ASTM B111 / ASME SB111 C68700 (CuZn20Al2As) ، أنبوب نحاسي من الألومنيوم ، O61 ، 19.05 × 1.65 × 6096 مم ، مكثف وتطبيق تبريد
|
1. Scope 1.1 This specification covers seamless tube and ferrule stock of copper and various copper alloys up 31/8 in, inclusive, in dimeter, for use in surface condensers, evaporators, and heat exchangers. tubes for this application are normally made from the following coppers or copper alloys: |
| Copper or Copper Alloy | Previousoy Use | Type of Metal |
| UNS No | Designaation | |
| C10200 | OF | Oxygen-free without residual deoxidants |
| C12000 | DLP | Phosphorixed, low residual phosphorus |
| C12200 | DHP | Phosphorized, high residual phosphorus |
| C14200 | DPA | Phophorized, arsenical |
| C19200 | - | Phophorized, 1% iron |
| C23000 | - | Red brass |
| C28000 | - | Muntz Metal |
| C44300 | - | Admiralty Metals,B,C,and D |
| C44400 | - | - |
| C44500 | - | - |
| C60800 | - | Aluminum Bronze |
| C68700 | - | Aluminum Brass, B |
| C70400 | - | 95-5 Copper-Nikel |
| C70600 | - | 90-10 Copper-Nikel |
| C71000 | - | 80-20 Copper-Nikel |
| C71500 | - | 70-30 Copper-Nikel |
| C71640 | - | Copper-Nikel-iron-Manganese |
| C72200 | - | - |
لسبائك النحاس التي يحدد فيها الزينيك بالباقي. يمكن اعتبار أي من النحاس أو الزنك هو الفرق
بين مجموع كل العناصر التي تم تحليلها و 100٪
الجدول 1 المتطلبات الكيميائية
| Composition, % | |||||||||||||
| Copper or Copper Alloy UNS No. | CopperA | Tin | Aluminum | Nickel, incl Cobalt | Lead, max | Iron | Zinc | Managnese | Arsenic | Antimony | Phosphorus |
Chro mium |
Other Named Elements |
| C10200 | 99.95 min | - | - | - | - | - | - | - | - | - | - | - | - |
| C12000 | 99.90 min | - | - | - | - | - | - | - | - | - | 0.004-0.012 | - | - |
| C12200 | 99.9 min | - | - | - | - | - | - | - | - | - | 0.015-0.040 | - | - |
| C14200 | 99.40 min | - | - | - | - | - | - | - | 0.15-0.50 | - | 0.015-0.040 | - | - |
| C19200 | 98.7 min | - | - | - | - | 0.8-1.2 | - | - | 0.15-0.50 | - | 0.01-0.04 | - | - |
| C23000 | 84.0-86.0 | - | - | - | 0.05 | 0.05 max | remalnder | - | - | - | - | - | - |
| C28000 | 59.0-63.0 | - | - | - | 0.30 | 0.07 max | remainder | - | - | - | - | - | - |
| C44300 | 70.0-73.0 | 0.9-1.2 | - | - | 0.07 | 0.06 max | remainder | - | 0.02-0.06 | - | - | - | - |
| C44400 | 70.0-73.0 | 0.9-1.2 | - | - | 0.07 | 0.06 max | remainder | - | - | 0.02-0.10 | - | - | - |
| C44500 | 70.0-73.0 | 0.9-1.2 | - | - | 0.07 | 0.06 max | remainder | - | - | - | 0.02-0.10 | - | - |
| C60800 | remainder | - | 5.0-6.5 | - | 0.10 | 0.10 max | - | - | 0.02-0.35 | - | - | - | - |
| C68700 | 76.0-79.0 | - | 1.8-2.5 | - | 0.07 | 0.06 max | remainder | - | 0.02-0.10 | - | - | - | - |
| C70400 | remainder | - | 4.8-6.2 | 0.05 | 1.3-1.7 | 1.0max | 0.30-0.8 | - | - | - | - | - | |
| C70600 | remainder | - | 9.0-11.0 | 0.05B | 1.0-1.8 | 1.0maxB | 1.0max | - | - | B | - | B | |
| C71000 | remainder | - | 19.0-23.0 | 0.05B | 0.50-1.0 | 1.0maxB | 1.0max | - | - | B | - | B | |
| C71500 | remainder | - | 29.0-33.0 | 0.05B | 0.40-1.0 | 1.0maxB | 1.0max | - | - | B | - | B | |
| C71640 | remainder | - | 29.0-32.0 | 0.05B | 1.7-2.3 | 1.0maxB | 1.5-2.5 | - | - | B | - | B | |
| C72200 | remainder | - | 15.0-18.0 | 0.05B | 0.50-1.0 | 1.0maxB | 1.0max | - | - | B |
0.30 -0.70 |
B | |
والنحاس (بما في ذلك الفضة)،
B عندما يكون المنتج مخصصًا لتطبيقات اللحام اللاحقة ، وعلى هذا النحو المحدد من قبل المشتري ، يجب أن يكون الزنك 0.50٪ كحد أقصى ،
الرصاص 0.02٪ كحد أقصى ، الفوسفور 0.02٪ كحد أقصى ، كبريت 0.02٪ كحد أقصى ، وكربون 0.05٪ كحد أقصى.
عندما يتم تحليل جميع العناصر في الجدول 1 ، يجب أن يكون مجموعها كما هو موضح في الجدول التالي.
| Copper Alloy UNS No. | Copper Plus Named Elements.% min |
| C23000 | 99.8 |
| C28000 | 99.7 |
| C44300 | 99.6 |
| C44400 | 99.6 |
| C44500 | 99.6 |
| C68700 | 99.5 |
الجدول 2 متطلبات الشد
| Copper or Copper Alloy UNS No. | Temper Designation | Tensile Strength min ksiA | Yield strengthBmin ksiA | Elongation in 2 in, min% | |
| Standard | Former | ||||
| C10200, C12000, C12200, C14200 | H55 | light-drawn | 36 | 30 | ... |
| C10200, C12000, C12200, C14200 | H80 | hard-drawn | 45 | 40 | ... |
| C19200 | 061 | annealed | 38 | 12 | ... |
| C23000 | 061 | annealed | 40 | 12 | ... |
| C28000 | 061 | annealed | 50 | 20 | ... |
| C44300, C44400, C44500 | 061 | annealed | 45 | 15 | ... |
| C60800 | 061 | annealed | 50 | 19 | ... |
| C68700 | 061 | annealed | 50 | 18 | ... |
| C70400 | 061 | annealed | 38 | 12 | ... |
| C70400 | H55 | light-drawn | 40 | 30 | ... |
| C70600 | 061 | annealed | 40 | 15 | ... |
| C70600 | H55 | light-drawn | 45 | 35 | ... |
| C71000 | 061 | annealed | 45 | 16 | ... |
| C71500 | 061 | annealed | 52 | 18 | ... |
| C71500 | - | - | - | - | - |
| Wall thicknesses up to 0.048 in, incl | HR50 | drawn, stress-relieved | 72 | 50 | 12 |
| Wall thicknesses over 0.048 in. | HR50 | drawn, stress-relieved | 72 | 50 | 15 |
| C71640 | 061 | annealed | 63 | 25 | ... |
| C71640 | HR50 | drawn, stress relieved | 81 | 58 | ... |
| C72200 | 061 | annealed | 45 | 16 | ... |
| C72200 | H55 | light-drawn | 50 | 30 | ... |
متطلبات التوسيع الجدول 3
| Temper Designatio | Copper or Copper Alloy UNS No. | Expansion of Tbue Outside Diameter, in Percent of Original Outside Diameter | |
| Standard | Former | ||
|
061 |
annealed |
C19200 | 30 |
| C23000 | 20 | ||
| C28000 | 15 | ||
| C44300,C44400,C44500 | 20 | ||
| C60800 | 20 | ||
| C68700 | 20 | ||
| C70400 | 30 | ||
| C70600 | 30 | ||
| C71000 | 30 | ||
| C71500 | 30 | ||
| C71640 | 30 | ||
| C72200 | 30 | ||
|
H55 |
light-drawn |
C10200,C12000,C12200 | 20 |
| C14200 | 20 | ||
| C70400 | 20 | ||
| C70600 | 20 | ||
| C72200 | 20 | ||
|
HR50 |
drawn,stress relieved | C71500 | 20 |
| hard-drawn, end annealed | C10200,C12000,C14200 | 30 | |
الجدول 4 عمق الشق
| Tube Wall Thickness, in. | Tube Outside Diameter, in. | ||
| Over ¼to ¾, incl | Over ¾ to 1 ¼, incl | Over 1¼ to 3⅓, incl. | |
| Over 0.017-0.032 | 0.005 | 0.006 | 0.007 |
| 0.032-0.049, incl | 0.006 | 0.006 | 0.0075 |
| 0.049-0.083, incl | 0.007 | 0.0075 | 0.008 |
| 0.083-0.109, incl | 0.0075 | 0.0085 | 0.0095 |
| 0.109-0.120, incl | 0.009 | 0.009 | 0.011 |
جدول 5 أقطار من الثقوب المحفورة
| Tube Outside Diameter, in. | Diameter of Drilled Holes, in. | Drill No. |
| ¼-¾, incl | 0.025 | 72 |
| Over ¾-1, incl | 0.031 | 68 |
| Over 1-1¼, incl | 0.036 | 64 |
| Over 1¼-1½, incl | 0.042 | 58 |
| Over 1½-1¾, incl | .0046 | 56 |
| Over 1¾-2, incl | 0.052 | 55 |
الاختبار الهيدروستاتيكي - يجب أن يقف كل أنبوب ، دون إظهار دليل على التسرب ، ضغط هيدروستاتيكي داخلي
يكفي لإخضاع المادة لضغط ليفي قدره 7000 رطل / بوصة مربعة ، تحدده المعادلة التالية لجوف رفيع
اسطوانات تحت التوتر. لا يلزم اختبار الأنبوب عند ضغط هودروستاتيكي يزيد عن 1000 رطل / بوصة مربعة ما لم يتم تحديد ذلك.
P = 2St / (D-0.8t) حيث:
P = الضغط الهيدروستاتيكي ، psig.
ر = سمك جدار الأنبوب ، بوصة.
D = القطر الخارجي للأنبوب. في و
S = الضغط المسموح به للمادة ، psi.
جدول 6 التسامح مع القطر
| Outside Diameter, in | Wall Thickness, in. | ||||
|
0.020A 0.022 0.025 0.028 |
0.032 | 0.035 | 0.042 | 0.049 and Over | |
| Diameter Tolerance, Plus and Minus, in. | |||||
| Up to 0.500, incl | 0.003 | 0.0025 | 0.0025 | 0.0025 | 0.0025 |
| Over 0.500-0.740, incl | 0.0040 | 0.004 | 0.004 | 0.0035 | 0.003 |
| Over 0.500-7.40, incl | 0.0060 | 0.006 | 0.005 | 0.0045 | 0.004 |
| Over 0.740-1.000, incl | ... | 0.009 | 0.008 | 0.006 | 0.045 |
| Over 1.250-1.375, incl | ... | ... | ... | 0.008 | 0.005 |
| Over 1.375-2.000, incl | ... | ... | ... | ... | 0.006 |
تسري التفاوتات في هذا العمود على درجات الحرارة المسحوبة والمرسومة بالضوء فقط.
يجب أن تكون التفاوتات في الأجواء الملدنة على النحو المتفق عليه بين الشركة المصنعة والمشتري.
الجدول 7 التسامح مع سماكة الجدار ، زائد وناقص.
| Wall Thicness, in. | Outside Diameter, in. | ||
| Over ⅛ to ⅝, incl | Over ⅝ to 1, incl | Over 1 to 2, incl | |
| 0.020, incl to 0.032 | 0.003 | 0.003 | ... |
| 0.032, incl to 0.035 | 0.003 | 0.003 | 0.004 |
| 0.035, incl to 0.058 | 0.004 | 0.0045 | 0.0045 |
| 0.058, incl to 0.083 | 0.0045 | 0.005 | 0.005 |
| 0.083, incl to 0.120 | 0.005 | 0.0065 | 0.0065 |
| 0.120, incl to 0.134 | 0.007 | 0.007 | 0.0075 |
الجدول 8 تحمّل الطول
| Specified Length, ft | Tolerance, all Plus, in. |
| Up to 15 | 3/32 |
| Over 15-20, incl | 1/8 |
| Over 20-30, incl | 5/32 |
| Over 30-60, incl | 3/8 |
| Over 60-100, inclA | 1/2 |
أنابيب مكثف في أطوال أكثر من 100 قدم ليست في الطلب الحالي. سيتم تطوير قيم التسامح للأطوال
حسب ما تمليه التجربة. قيم التسامح للأطوال في سمك الجدار 0.020 ، بما في ذلك. إلى 0.032 على النحو المتفق عليه
بين الصانع أو المورد والمشتري.
| Tube. Outside Diameter, in | Tolerance |
| Up to ⅝, incl | 0.010 in. |
| Over ⅝ | 0.016 in./in. of diameter |
يجب أن تكون الخصائص والتركيبات الكيميائية المذكورة في هذه المواصفة ، في حالة الاختلاف ،
يتم تحديدها وفقًا لطرق ASTM التالية:
| Test | ASTM Designation |
| Chemical analysis | B 170A,E53,E54,E62,E75,E478 |
| Grainsize | E112 |
| Expansion (pin test) | B153 |
| Mercurous nitrate | B154 |
| Tension | E8 |
| Nondestructive test | E243 |
تشير الإشارة إلى المواصفة B170 إلى الطرق الكيميائية المقترحة في ملحقها.
عندما اختبرت لجنة E-1 ونشرت طرقًا لمعايرة النتوءات منخفضة المستوى في النحاس.
سيتم إلغاء ملحق المواصفات ب 170.
الملاحق (معلومات غير إلزامية)
X1. كثافة سبائك النحاس والنحاس
X1.1 ترد كثافات السبائك التي تغطيها هذه المواصفات في الجدول X1.1.
كثافة الجدول X1.1
| Copper or Copper Alloy UNS No. | Density, lb.in.3 |
| C10100,C10200,C10300,C10800,C12000,C12200,C14200 | 0.323 |
| C19200 | 0.320 |
| C23000 | 0.316 |
| C28000 | 0.303 |
| C44300,C44400,C44500 | 0.308 |
| C60800 | 0.295 |
| C61300,C61400 | 0.285 |
| C68700 | 0.301 |
| C70400 | 0.323 |
| C70600 | 0.323 |
| C71000 | 0.323 |
| C71500 | 0.323 |
| C71640 | 0.323 |
| C72200 | 0.323 |
جداول مقارنة المواد (ASTM → KS و JIS و DIN و BS و NBN و NF و UNI)
| ASTMSTANDARD | UNS NO. | KOREA/JAPANES | GERMAN | BRITISH | ISO | ||||||
| KS/JIS Symbol | KS/JIS Numbe | DIN Type | DIN Number | Materiral Number | B.S Number | B.S Grade | Remarks | ISO Type | ISO Number | ||
| B 111 Copper and Copper-Alloy Seamless Condenser Tube and Ferrule Stock | |||||||||||
| C44300 | C44300 | C4430T/C4430T | D5301/H3300 | CuZn28Sn | 1785 | 2871 | CZ111 | CuZn28Sn1 | R1337 | ||
| C68700 | C68700 | C6870T/C6870T | D5301/H3300 | CuZN20Al | 1785 | 2871 | CZ110 | CuZn20Al2 | 426-I | ||
| C70600 | C70600 | C7060T/C7060T | D5301/H3300 | CuNi10Fe1Mn | 17664 | 2871 | CN102 | CuNi10Fe1Mn | 429 | ||
| C71000 | C71000 | C7100T/C7100T | D5301/H3300 | ||||||||
| C71500 | C71500 | C7150T/C7150T | D5301/H3300 | CuNi30Mn1Fe | 17664 | 2871 | CN107 | CuNi30Mn1Fe | |||
| C71640 | C71640 | C7164T/C7164T | D5301/H3300 | CuNi30Fe2Mn2 | 17664 | 2871 | CN108 | CuNi3 | |||
| بيع الوحدات | : | Piece/Pieces |
|---|
The file is encrypted. Please fill in the following information to continue accessing it
الدفع نوع: L/C,T/T
إنكوترم: FOB,CFR,CIF,EXW
ابقى على تواصل
If you have any questions our products or services,feel free to reach out to us.Provide unique experiences for everyone involved with a brand.we’ve got preferential price and best-quality products for you.
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.